We are committed to providing one-stop service for steel pipe products to customers around the world.
Centerway steel co.,ltd can provide LSAW (Longitudinal double submerge arc welding) carbon steel pipe of various standards and grades, passed ISO9001, SGS and other certificates, accept third-party testing, has complete testing and testing facilities, from product development, raw material supply, production process management, etc. in accordance with international quality The system standards are standardized to provide customers with satisfactory pre-sale, in-sale and after-sale services. Feel free to contact us anytime
LSAW (Longitudinal double submerge arc welding) carbon steel pipe is a type of SAW pipe made of steel plates that were hot rolled by JCOE forming technology. JCOE technology represents the shaping and forming processes involved during manufacturing as well as the inner and outer welding and cold expansion carried out after welding.
|
Usage |
O.D.(mm) |
W.T.(mm) |
Length(m) |
|
Oil &gas pipeline |
406-1524(16” – 60”) |
6-40 (1/4” – 1.57”) |
8-12.1 |
|
for Construction(Pipe Piles) |
350-1600(14” – 63”) |
6-60 (1/4” – 2.36”) |
6-12 |
|
Roller pipe |
1200-3800(47.24” – 150”) |
12-120 (1/2”- 4.7”) |
<=3.2 |
|
Addition to above specification, the pipes can be produced according to customer’s requirements |
|||
Tolerance of Outside Diameter and Wall Thickness
|
Types |
Standard |
|||||
|
SY/T5040-2000 |
SY/T5037-2000 |
SY/T9711.1-1977 |
ASTM A252 |
AWWA C200-97 |
API 5L PSL1 |
|
|
Tube end OD deviation |
±0.5%D |
±0.5%D |
-0.79mm～+2.38mm |
<±0.1%T |
<±0.1%T |
±1.6mm |
|
Wall thickness |
±10.0%T |
D<508mm, ±12.5%T |
-8%T～+19.5%T |
<-12.5%T |
-8%T～+19.5%T |
5.0mm |
|
D>508mm, ±10.0%T |
T≥15.0mm, ±1.5mm |
|||||
|
O.D. |
W.T. |
Length(m) |
|||||||
|
Inch |
mm |
Min.Yield Strength(Mpa) |
|||||||
|
Inch |
mm |
245(B) |
290(X42) |
360(X52) |
415(X60) |
450(X65) |
485(X70) |
555(X80) |
|
|
16 |
406 |
6.0-14.0 |
6.0-13.0 |
6.0-12.0 |
6.0-11.0 |
6.0-10.5 |
6.0-10.0 |
6.0-9.0 |
6.0-12.3 |
|
18 |
457 |
6.0-15.0 |
6.0-14.0 |
6.0-13.0 |
6.0-12.0 |
6.0-11.5 |
6.0-11.0 |
6.0-10.0 |
6.0-12.3 |
|
20 |
508 |
6.0-16.0 |
6.0-15.0 |
6.0-14.0 |
6.0-13.0 |
6.0-12.5 |
6.0-12.0 |
6.0-11.0 |
6.0-12.3 |
|
22 |
559 |
6.0-17.0 |
6.0-16.0 |
6.0-15.0 |
6.0-14.0 |
6.0-13.5 |
6.0-13.0 |
6.0-12.0 |
6.0-12.3 |
|
24 |
610 |
6.0-18.0 |
6.0-17.0 |
6.0-16.0 |
6.0-15.0 |
6.0-14.5 |
6.0-14.0 |
6.0-13.0 |
6.0-12.3 |
|
26 |
660 |
6.0-19.0 |
6.0-18.0 |
6.0-17.0 |
6.0-16.0 |
6.0-15.0 |
6.0-15.0 |
6.0-14.0 |
6.0-12.3 |
|
28 |
711 |
6.0-20.0 |
6.0-19.0 |
6.0-18.0 |
6.0-17.0 |
6.0-16.5 |
6.0-16.0 |
6.0-15.0 |
6.0-12.3 |
|
30 |
762 |
7.0-21.0 |
7.0-20.0 |
7.0-19.0 |
7.0-18.0 |
7.0-17.5 |
7.0-17.0 |
7.0-16.0 |
6.0-12.3 |
|
32 |
813 |
7.0-22.0 |
7.0-21.0 |
7.0-20.0 |
7.0-19.0 |
7.0-18.5 |
7.0-18.0 |
7.0-17.0 |
6.0-12.3 |
|
34 |
864 |
7.0-23.0 |
7.0-22.0 |
7.0-21.0 |
7.0-20.0 |
7.0-19.5 |
7.0-19.0 |
7.0-18.0 |
6.0-12.3 |
|
36 |
914 |
8.0-24.0 |
8.0-23.0 |
8.0-22.0 |
8.0-21.0 |
8.0-20.5 |
8.0-20.0 |
8.0-19.0 |
6.0-12.3 |
|
38 |
965 |
8.0-25.0 |
8.0-24.0 |
8.0-23.0 |
8.0-22.0 |
8.0-21.5 |
8.0-21.0 |
8.0-20.0 |
6.0-12.3 |
|
40 |
1016 |
8.0-26.0 |
8.0-25.0 |
8.0-24.0 |
8.0-23.0 |
8.0-22.5 |
8.0-22.0 |
8.0-21.0 |
6.0-12.3 |
|
42 |
1067 |
8.0-26.0 |
8.0-25.0 |
8.0-24.0 |
8.0-23.0 |
8.0-22.5 |
8.0-22.0 |
8.0-21.0 |
6.0-12.3 |
|
44 |
1118 |
9.0-27.0 |
9.0-26.0 |
9.0-24.5 |
9.0-23.5 |
9.0-22.8 |
9.0-22.0 |
9.0-21.0 |
6.0-12.3 |
|
46 |
1168 |
9.0-27.0 |
9.0-26.0 |
9.0-24.0 |
9.0-23.5 |
9.0-22.8 |
9.0-22.0 |
9.0-21.0 |
6.0-12.3 |
|
48 |
1219 |
9.0-28.0 |
9.0-27.0 |
9.0-25.4 |
9.0-24.0 |
9.0-23.5 |
9.0-23.0 |
9.0-22.0 |
6.0-12.3 |
|
52 |
1321 |
9.0-28.0 |
9.0-27.0 |
9.0-25.4 |
9.0-24.2 |
9.0-23.5 |
9.0-23.0 |
9.0-22.0 |
6.0-12.3 |
|
56 |
1422 |
10.0-29.0 |
10.0-28.0 |
10.0-26.0 |
10.0-24.5 |
10.0-23.8 |
10.0-23.0 |
10.0-22.0 |
6.0-12.3 |
|
60 |
1524 |
10.0-29.0 |
10.0-28.0 |
10.0-26.0 |
10.0-24.5 |
10.0-23.8 |
10.0-23.0 |
10.0-22.0 |
6.0-12.3 |
|
64 |
1626 |
10.0-30.0 |
10.0-29.0 |
10.0-27.0 |
10.0-25.4 |
10.0-24.8 |
10.0-24.0 |
10.0-23.0 |
6.0-12.3 |
|
68 |
1727 |
10.0-30.0 |
10.0-29.0 |
10.0-27.0 |
10.0-25.4 |
10.0-24.8 |
10.0-24.0 |
10.0-23.0 |
6.0-12.3 |
|
72 |
1829 |
10.0-30.0 |
10.0-29.0 |
10.0-27.0 |
10.0-25.4 |
10.0-24.8 |
10.0-24.0 |
10.0-23.0 |
6.0-12.3 |
Standard:
ASTM 53
API Spec 5L
ASTM A252-89, EN10217, EN10219
Steel grades:
API 5L: GR A, GR B, X42, X46, X56, X60, X65, X70
ASTM A252 GR 1, GR 2, GR 3
ASTM A53: GR A, GR B, GR C, GR D
BS 4360: Grade 43, Grade 50
EN: S275, S275JR, S355JRH, S355J2H
Chemical Composition and Mechanical Properties
|
Standard |
Grade |
Chemical Composition(max)% |
Mechanical Properties(min) |
|||||
|
C |
Mn |
Si |
S |
P |
Yield Strength (Mpa) |
Tensile Strength (Mpa) |
||
|
GB/T700-2006 |
A |
0.22 |
1.4 |
0.35 |
0.050 |
0.045 |
235 |
370 |
|
B |
0.2 |
1.4 |
0.35 |
0.045 |
0.045 |
235 |
370 |
|
|
C |
0.17 |
1.4 |
0.35 |
0.040 |
0.040 |
235 |
370 |
|
|
D |
0.17 |
1.4 |
0.35 |
0.035 |
0.035 |
235 |
370 |
|
|
GB/T1591-2009 |
A |
0.2 |
1.7 |
0.5 |
0.035 |
0.035 |
345 |
470 |
|
B |
0.2 |
1.7 |
0.5 |
0.030 |
0.030 |
345 |
470 |
|
|
C |
0.2 |
1.7 |
0.5 |
0.030 |
0.030 |
345 |
470 |
|
|
BS En10025 |
S235JR |
0.17 |
1.4 |
- |
0.035 |
0.035 |
235 |
360 |
|
S275JR |
0.21 |
1.5 |
- |
0.035 |
0.035 |
275 |
410 |
|
|
S355JR |
0.24 |
1.6 |
- |
0.035 |
0.035 |
355 |
470 |
|
|
DIN 17100 |
ST37-2 |
0.2 |
- |
- |
0.050 |
0.050 |
225 |
340 |
|
ST44-2 |
0.21 |
- |
- |
0.050 |
0.050 |
265 |
410 |
|
|
ST52-3 |
0.2 |
1.6 |
0.55 |
0.040 |
0.040 |
345 |
490 |
|
|
JIS G3101 |
SS400 |
- |
- |
- |
0.050 |
0.050 |
235 |
400 |
|
SS490 |
- |
- |
- |
0.050 |
0.050 |
275 |
490 |
|
|
API 5L PSL1 |
A |
0.22 |
0.9 |
- |
0.03 |
0.03 |
210 |
335 |
|
B |
0.26 |
1.2 |
- |
0.03 |
0.03 |
245 |
415 |
|
|
X42 |
0.26 |
1.3 |
- |
0.03 |
0.03 |
290 |
415 |
|
|
X46 |
0.26 |
1.4 |
- |
0.03 |
0.03 |
320 |
435 |
|
|
X52 |
0.26 |
1.4 |
- |
0.03 |
0.03 |
360 |
460 |
|
|
X56 |
0.26 |
1.1 |
- |
0.03 |
0.03 |
390 |
490 |
|
|
X60 |
0.26 |
1.4 |
- |
0.03 |
0.03 |
415 |
520 |
|
|
X65 |
0.26 |
1.45 |
- |
0.03 |
0.03 |
450 |
535 |
|
|
X70 |
0.26 |
1.65 |
- |
0.03 |
0.03 |
585 |
570 |
|